Dilatometric investigations of Fe – Cr – Mo – C system

Автори

  • Maciej Sulowski AGH University of Science and Technology Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, Mickiewicz 30 Ave., 30-059 Krakow, Poland
  • Ewa Lichańska AGH University of Science and Technology Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, Mickiewicz 30 Ave., 30-059 Krakow, Poland
  • Paweł Kulecki AGH University of Science and Technology Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, Mickiewicz 30 Ave., 30-059 Krakow, Poland
  • Monika Tenerowicz-Żaba AGH University of Science and Technology Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, Mickiewicz 30 Ave., 30-059 Krakow, Poland
  • Anna Staniek AGH University of Science and Technology Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, Mickiewicz 30 Ave., 30-059 Krakow, Poland

DOI:

https://doi.org/10.29114/ajtuv.vol2.iss2.79

Ключови думи:

Powder metallurgy, sintered steels, dilatometric investigation, phase transformation

Абстракт

Sintering behavior in high purity nitrogen and mixture of 5% H2-95% N2 of Fe-(Cr)-(Mo)-C system was investigated. The mixtures, differ from chromium, molybdenum and carbon content were prepared in Turbula mixer. Then, using single-action pressing in a rigid die at pressing pressure 400 MPa, green compacts with density level 5.9±0.17 g/cm3 were pressed. Sintering was carried out in a horizontal push rod dilatometer Netzsch 402E at 1120 and 1250°C for 60 min. Heating and cooling rates were 10 and 20°C/min., respectively. After heating, compacts were isothermal sintered at 1120 or 1250°C for 60 minutes an cooled up to 200°C, then isothermally hold for 60 minutes and definitely cooled to the room temperature. Pure nitrogen and mixture of 5% H2-95% N2 were employed as sintering atmospheres. During investigations the influence of isothermal sintering temperature, chemical composition of sintering atmosphere, chromium, molybdenum and carbon content was followed by dilatometry. The aim of investigations was to determine transformation temperatures. It was shown that the dimensional changes occurring during heating and isothermal sintering and the final density of sintered compacts are influenced by sintering parameters and the alloying elements concentration in powder mixture.

Изтегляния

Данни за теглене още не са налични.

References

<p>Ciaś, A. (1992). Zarys metalurgii proszk&oacute;w. Warszawa. Polska: WSziP.<br />&nbsp;<br />Ciaś, A. (2004). Development and Properties of Fe-Mn-(Mo)-(Cr)-C Sintered Structural Steels. Krak&oacute;w: AGH.<br />PMid:15473734<br />&nbsp;<br />Ciaś, A. (2013). Effect of local sintering microatmosphere on mechanical properties of Fe &ndash; 3Cr-0.5Mo -0.6C steel. Powder Metallurgy, 56(3), 231.&nbsp;<br /><a href="https://doi.org/10.1179/1743290112Y.0000000048" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />Ciaś, A., Mitchell, S. C., Pilch, K., Ciaś, H., Sułowski, M., &amp; Wroński, A. S. (2003). Tensile properties of Fe-3Mn-0.6/0.7C steels sintered in semiclosed containers in dry hydrogen, nitrogen and mixtures thereof. Powder Metallurgy, 46(2), 165&ndash;170.&nbsp;<br /><a href="https://doi.org/10.1179/003258903225005312" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />Cygan, S., (2013). Obr&oacute;bka cieplna spiekanych stali manganowo-chromowo-molibdenowych. Krak&oacute;w: AGH<br />PMCid:PMC5452775<br />&nbsp;<br />Gac, P., (2012). Własności mechaniczne i mikrostruktura spiekanych stali o zawartości 3% Mn, 3% Cr i 0,5% Mo obrobionych cieplnie. Krak&oacute;w: AGH.<br />&nbsp;<br />German, R. M. (1994). Powder metallurgy science second edition. Princeston: MPIF.<br />&nbsp;<br />Klein, A. N., Oberacker, R., &amp; Thummler, F. (1985a). High Strength Si-Mn-Alloyed Sintered Steels - Microstructure and Mechanical Properties. Powder Metallurgy International, 17(2), 13&ndash;16.<br />&nbsp;<br />Klein, A. N., Oberacker, R., &amp; Thummler, F. (1985b). High strength Si-Mn-alloyed sintered steels &ndash; Sinterability and homogenization. Powder Metall Int., 17(2), 71.<br />&nbsp;<br />Kulecki, P., (2013). Własności mechaniczne i struktura spiekanych stali konstrukcyjnych. Krak&oacute;w: AGH.<br />&nbsp;<br />Lichańska, E., (2014). Wpływ parametr&oacute;w wytwarzania na własności spiekanych stali Mn-Cr-Mo o niskiej zawartości węgla. Krak&oacute;w: AGH.<br /><br />Mazahery, A., &amp; Shabani, M. (2012). Characterization of wear mechanisms in sintered Fe-1.5 wt % Cu alloys. Archives of Metallurgy and Materials, 57(1), 93&ndash;103.&nbsp;<br /><a href="https://doi.org/10.2478/v10172-011-0158-x" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />Missol, W. (1972). Spiekane części maszyn. Katowice. Polska: Śląsk<br />&nbsp;<br />Hryha, E., Čajkova, E.&amp; Dudrov&aacute; E. (2007). Study of reduction/oxidation processes in Cr-Mo prealloyed steels during sintering by continuous atmosphere monitoring. Powder Metallurgy Progress, 7(4), 181-197.<br />&nbsp;<br />&Scaron;alak, A. (1980a). Sintered Manganese Steels, Part I: Effect of Structure of Initial Iron Powders Upon Mechanical Properties. Powder Metallurgy International, 12(1), 28&ndash;31.<br />&nbsp;<br />&Scaron;alak, A. (1980b). Sintered Manganese Steels, Part II: Manganese Evaporation During Sintering. Powder Metallurgy International, 12(2), 72&ndash;75.<br />&nbsp;<br />&Scaron;alak, A., &amp; Seleck&aacute;, M. (2012). Manganese in Powder Metallurgy Steels. Cambridge International Science Publishing Ltd.&nbsp;<br /><a href="https://doi.org/10.1007/978-1-907343-75-9" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />Sułowski, M., &amp; Ciaś, A. (2011). Microstructure and mechanical properties of Cr-Mn structural PM steels. Archives of Metallurgy and Materials, 56(2), 293&ndash;304.&nbsp;<br /><a href="https://doi.org/10.2478/v10172-011-0033-9" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />Bergman, O. &amp; Bengston, S. (2009). Influence of sintering temperature and component density on the properties of prealloyed PM steel grades containing Cr, Mo and Mn. In Proc. of EuroPM 2009, Copenhagen, Sweden, v. 1, Sintered steels II &ndash; Sinterhardening, p. 35-40.<br />&nbsp;<br />Zapf, G., Hoffmann, G., &amp; Dalal, K. (1975). Effect of additional alloying elements on the properties of sintered manganese steels. Powder Metallurgy, 18(35), 214&ndash;236.&nbsp;<br /><a href="https://doi.org/10.1179/pom.1975.18.35.014" target="_blank" rel="noopener">Crossref</a><br />&nbsp;<br />North American H&ouml;gan&auml;s handbook for iron and steel powders for sintered components (2002). H&ouml;gan&auml;s AB.</p>

Downloads

Публикуван

2018-12-21

How to Cite

Sulowski, M., Lichańska, E., Kulecki, P., Tenerowicz-Żaba, M., & Staniek, A. (2018). Dilatometric investigations of Fe – Cr – Mo – C system. ГОДИШНИК НА ТЕХНИЧЕСКИ УНИВЕРСИТЕТ - ВАРНА, 2(2), 1–13. https://doi.org/10.29114/ajtuv.vol2.iss2.79

Брой

Т. 2 Бр. 2 (2018): Годишник на Технически Университет - Варна

Раздел (Секция)

МЕХАНИКА, МАТЕРИАЛИ И МАШИННО ИНЖЕНЕРСТВО

License

          СПОРАЗУМЕНИЕ ЗА ПУБЛИКУВАНЕ

           Годишника на Технически университет - Варна (ГТУВ) цели да гарантира, че постъпващите статии се публикуват, като същевременно се предоставя значителна свобода на публикуващите ги автори. За изпълнение на тази цел, ГТУВ поддържа гъвкава политика относно авторските права, което означава, че няма прехвърляне на авторски права от автора на издателя, а авторите запазват изключително авторско право върху интелектуалното си произведение.

           При изпращане на статия, Отговорния автор трябва да се съгласи и приеме правилата и условията за публикуване, изложени в настоящото Споразумение за публикуване, които са както следва:

          ПРЕДОСТАВЯНЕ НА ПРАВА ОТ ОТГОВОРНИЯ АВТОР
           Отговорния автор предоставя на ГТУВ за времето на пълния срок на авторското право и всяко следващо удължаване или подновяване, следното:
      • Неотменимо, неизключително право да публикува, възпроизвежда, предоставя, разпространява или по друг начин използва предоставената работа в електронни и печатни издания и в производни произведения в целия свят, на всички езици и във всички известни съществуващи или в последствие възникнали медии.
      • Неотменимо, неизключително право да създава и съхранява електронни архивни копия на работата, включително правото да депозира предоставената работа в дигитални хранилища с отворен достъп.
      • Неотменимо, неизключително право на лицензиране на други лица да възпроизвеждат, превеждат, преиздават, предоставят и разпространяват предоставената работа при условие, че авторите са надлежно идентифицирани (за момента това се извършва чрез публикуване на произведението под лиценз Creative Commons Attribution 4.0 Unported).
           С предоставянето на работата за публикуване, авторските права върху материала остават на авторите. Авторите запазват всички патентни, търговски марки и/или други права върху интелектуалната си собственост.

           ЗАДЪЛЖЕНИЯ НА ОТГОВОРНИЯ АВТОР И СЪАВТОРИТЕ
           При последващо разпространение или повторно публикуване на предоставената работа, Отговорния автор се съгласява да идентифицира ГТУВ, в който е публикувано произведението като първоначален източник на първото публикуване на работата. Отговорния автор гарантира, че съавторите също ще посочват ГТУВ като източник на първото публикуване, когато разпространяват, преиздават или се позовават на настоящата работа в бъдещи свои публикации.

           ГАРАНЦИИ ОТ СТРАНА НА ОТГОВОРНИЯ АВТОР
          Отговорния автор гарантира че предоставената за публикуване работа не нарушава никои действащи нормативни разпоредби или законни права на която и да е трета страна. Същия гарантира че работата не съдържа какъвто и да е материал, който може да се възприеме от читателската аудитория като неетичен, компрометиращ, нехуманен, расистки, клеветнически и/или нарушаващ авторски и/или имуществени права, права на интелектуална собственост или поети ангажименти за поверителност към трети страни. Отговорния автор гарантира че предоставеният материал е с оригинално съдържание, не е официално публикуван в никое друго издателство, както и че не е в процес на публикуване пред други издателства. Отговорния автор също така гарантира че притежава съответните правомощия да сключи настоящото споразумение. Ако предоставяната работа е подготвена съвместно с други съавтори, Отговорния автор гарантира че всички останали съавтори са информирани и са съгласни предоставения материал да бъде публикуван в ГТУВ.

            Отговорния автор лично (или от името на авторския колектив) дава съгласието си да не въвлича по никакъв начин ГТУВ като страна в каквито и да било научни, академични, административни и/или съдебни спорове, в случаите на установени нарушения на горепосочените декларации и гаранции. 

           ПРАВА И ЗАДЪЛЖЕНИЯ НА ГТУВ
           ГТУВ се съгласява да публикува предоставения материал, в случаите когато същия отговаря напълно на всички необходими качествени, технически и редакционни изисквания, като го идентифицира еднозначно с авторите му. В следствие на настоящото споразумение, на ГТУВ се предоставя правомощие да упражнява права при необходимост от името на авторите върху трети лица, като например в случаите на установено плагиатство, нарушаване на авторски права и др.

           Декларация за поверителност на лични данни
             Вашите имена и имейл адреси, въведени в уебсайта на ГТУВ, ще бъдат използвани само и изключително за обявените цели на настоящото списание и няма да бъдат използвани за никакви други цели от издателя или предоставяни на друга - трета страна.
       Издателят се задължава да извърши всички необходими действия, цялата предоставена лична информация да остане конфиденциална, в рамките на издателя и да не бъде споделена с външни обекти или субекти, освен ако не е дадено предварително изрично разрешение от собственика на личните данни.
             Вашата лична информация няма да бъде обект на продажба, разпространение или публикуване по какъвто и да е начин и под каквато и да е форма.

Подобни статии

Можете също да прегледате стартирайте разширено търсене за подобни статии във връзка с тази статия.